Road marking paint series, including room temperature solvent type and hot melt reflective type, is suitable for traffic marking rerouting of asphalt or concrete pavement with various flow rates. It has many characteristics, such as hard paint film, wear resistance, weather resistance, good color retention and good adhesion of pavement. It is the preferred marking line for expressways, high-grade highways and large flow highways. Paint.
Species: JB86 road marking varnish can be divided into two types:
1. Hot-melt road reflective marking paint
Road reflective marking paint is a kind of small powder paint synthesized by using foreign high-quality resin, pigments, aggregates, additives and other chemical materials. Coatings melt into a thick film by heating at a suitable temperature. The film has bright color, strong recognition and excellent night reflective effect. Good construction performance, fast drying, strong bonding force, good wear resistance and durability, suitable for coating asphalt, concrete and other pavement. It is particularly suitable for coating fast urban roads and highways as signs and markings.
Two. Ambient temperature (Leng Tu) road marking paint
Cold painted road marking paint is made of resin, pigments and fillers and organic solvents. It has fast drying, medium resistance and good workability. Widely used in asphalt concrete pavement, and various factories, offices, schools, parking lot and field use. Three, suburban highways and freeway road markings are generally suitable for selecting hot-melt road reflective coatings.
Composition: single component coating consisting of acrylic resin, pigments and fillers, auxiliaries and solvents.
Characteristics: the film is tough and strong adhesion, excellent abrasion resistance, excellent water resistance, alkali resistance, weatherability, clear film, on the asphalt pavement not bleeding.
Application: suitable for marking marks on asphalt road.
Appearance: yellow, red and white.
Density: about 1.30 UU
Coating methods: roll coating, brush coating, spraying
Thinner: special diluent for JB86
Drying time: 232 degrees centigrade: 3 minutes dry, 10 minutes dry.
Painting interval: 232 C: shortest 1 hours.
Theoretical dosage: 320~350 g/m2
Film thickness: wet film: 250 m; dry film: 100 m;
Surface treatment: brush or roller coating construction, must take the same direction fast brushing, do not pour from brush, to prevent leakage of tar. Add dilution dose should be appropriate, not in hot sunshine direct construction, in order to prevent tar exudation.